Geomembrane



We furnish acme quality HDPE Geomembrane that is made from polymeric materials. HDPE Geomembrane is made using various ways except weaving methods as it leaves large voids in material. Some of the materials use in the manufacturing of Geomembrane is Polypropylene, Polyethylene, PVC and HDPE. In addition to this, Polyethylene Geomembrane has diverse applications that include Water Reservoir, Road Work, Land Filled Capping, Evaporation Pond, Air Field and many more. Available in different quantities, the Geomembrane offered can be availed at reasonable prices. We are tagged as one of the famed Geomembrane Manufacturers in India.

APPLICATION PRIMARY FUNCTION
Hazardous Solid Waste Land Filled Impervious barrier
Municipal Solid Waste Land Filled Impervious barrier
Road Work Impervious barrier
Air Field Impervious barrier
Water Reservoir Impervious barrier
Evaporation Pond Impervious barrier
Land Filled Capping Impervious barrier

Specifications

Property Test Method Nominal Values
Thickness, mm ASTM D 751/1593/5199 1 1.5 2 2.5 3
Density, g/cc ASTM D 792/1505 0.94 0.94 0.94 0.94 0.94
Strength at Break, N/mm ASTM D 6693, Type IV 34 52 69 86 103
Strength at Yield, N/mm ASTM D 6693, Type IV 16 25 33 41 50
Elongation at Break, % ASTM D 6693, Type IV 750 800 800 800 800
Elongation at Yield, % ASTM D 6693, Type IV 15 15 15 15 15
Tear Resistance, N ASTM D 1004 146 222 293 369 445
Puncture Resistance, N FTMS 101, Method 2065 267 400 533 667 800
Carbon Black Content, % ASTM D 1603 02/03/14 02/03/14 02/03/14 02/03/14 02/03/14
Carbon Black Dispersion ASTM D 3015 A1/A2 A1/A2 A1/A2 A1/A2 A1/A2
Dimensional Stability, % (each direction) ASTM D 1204, 100°C 1hr ±1 ±1 ±1 ±1 ±1
Environmental Stress Crack Resistance, hr ASTM D 1693, Cond. B >2000 >2000 >2000 >2000 >2000
Low Temperature Brittleness, °C ASTM D 746, Cond. B <-84 <-84 <-84 <-84 <-84
Oxidative Induction Time, minutes ASTM D 3895, 200°C Pure O2, 1 atm 100 100 100 100 100
Ozone Resistance ASTM D 1149, 7 days 100ppm No Cracks No Cracks No Cracks No Cracks No Cracks
Water Absorption, % wt. change ASTM D 570 <0.01 <0.01 <0.01 <0.01 <0.01
Moisture Vapour Transmission, g/m² ASTM E 96 <0.001 <0.001 <0.001 <0.001 <0.001
Melt Flow Index, g/10 minutes ASTM D 1238, Cond. 190/2.16 <=1.0 <=1.0 <=1.0 <=1.0 <=1.0